Preparation of magnetic nanocomposite beads and optimizing the conditions for effective removal of U(VI) from aqueous solutions

Abstract

Magnetic ion-imprinted polymers (IIPs) were prepared by precipitate polymerization and leached with HCl to remove uranium. Their ability to remove hexavalent uranium from wastewater effluents was studied. Batch adsorption studies to determine the optimum conditions of U(VI) removal were conducted at different levels of sample pH, sorbent amount, agitation time, and initial uranium concentration. It was observed that, under optimum conditions (i.e. pH 4, adsorbent amount of 50 mg, 45 min agitation time, and initial U(VI) concentration of 2 mg L−1), the maximum removal of U(VI) cations was >98% and 80% for the magnetic IIP and the corresponding magnetic non-imprinted polymers (NIP), respectively. Langmuir and Freundlich isotherms were used to describe the adsorption of U(VI) onto magnetic IIP and NIP. The adsorption capacity of U(VI) was determined to be 1.06 and 0.85 mg g−1 for the two isotherms, respectively. The order of selectivity was found to be U(VI) > Fe(III) > Pb(II). For six cycles of regeneration and reuse, the magnetic polymers maintained their stabilities with only a 4% loss in the extraction efficiency. The average extraction efficiencies of the magnetic polymers for the spiked acid mine drainage and sewage wastewater effluents were 71% and 58% for the magnetic IIP and NIP, respectively. From powder X-ray diffraction analysis, application of the Scherrer equation yielded magnetic nanoparticles of an average mean diameter of 11.9 nm. Thermo-gravimetric analysis revealed that the HCl-leached magnetic polymers had a magnetite residual weight of 5%.