Abstract
A high-purity Ti–48Al–2Nb–2Cr alloy powder with an oxygen content as low as 0.0572 wt.% and a particle size of <150 μm was produced from a mixture of TiO2, Al2O3, Nb2O5, and Cr2O3 powders through reduction with magnesium and deoxidation with calcium. The phase and composition of the products were analyzed. The final product mainly included γ-TiAl and minor α2-Ti3Al phases, and Ti, Al, Cr, and Nb were homogenously distributed in the powder with a mole ratio of 49.73:43.51:2.05:1.98. The reduction and deoxidation mechanisms were investigated by thermodynamic modeling using the HSC Chemistry software and Pandat software based on the Ti alloy database.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.