Preparation of Large-area Vertical 2D Crystal Hetero-structures Through the Sulfurization of Transition Metal Films for Device Fabrication.

Abstract

We have demonstrated that through the sulfurization of transition metal films such as molybdenum (Mo) and tungsten (W), large-area and uniform transition metal dichalcogenides (TMDs) MoS2 and WS2 can be prepared on sapphire substrates. By controlling the metal film thicknesses, good layer number controllability, down to a single layer of TMDs, can be obtained using this growth technique. Based on the results obtained from the Mo film sulfurized under the sulfur deficient condition, there are two mechanisms of (a) planar MoS2 growth and (b) Mo oxide segregation observed during the sulfurization procedure. When the background sulfur is sufficient, planar TMD growth is the dominant growth mechanism, which will result in a uniform MoS2 film after the sulfurization procedure. If the background sulfur is deficient, Mo oxide segregation will be the dominant growth mechanism at the initial stage of the sulfurization procedure. In this case, the sample with Mo oxide clusters covered with few-layer MoS2 will be obtained. After sequential Mo deposition/sulfurization and W deposition/sulfurization procedures, vertical WS2/MoS2 hetero-structures are established using this growth technique. Raman peaks corresponding to WS2 and MoS2, respectively, and the identical layer number of the hetero-structure with the summation of individual 2D materials have confirmed the successful establishment of the vertical 2D crystal hetero-structure. After transferring the WS2/MoS2 film onto a SiO2/Si substrate with pre-patterned source/drain electrodes, a bottom-gate transistor is fabricated. Compared with the transistor with only MoS2 channels, the higher drain currents of the device with the WS2/MoS2 hetero-structure have exhibited that with the introduction of 2D crystal hetero-structures, superior device performance can be obtained. The results have revealed the potential of this growth technique for the practical application of 2D crystals.