Abstract
Biocompatible hydroxyapatite (HA)/poly(vinyl alcohol) (PVA) composites and their transparent films were prepared by the coprecipitation and solvent casting method. The formation of HA in PVA composite powder was confirmed by the characteristic phosphate bands at 1100–1032 and 565 cm−1 at FT-IR spectra, and the weight ratio of HA to PVA was 50/50 examined by TGA. The crystal melting temperature of HA/PVA decreased compared with that of pure PVA. HA/PVA (50/50) composite powder and pure PVA were dissolved in dimethyl sulfoxide to obtain a film with HA/PVA weight ratio of 10/90. To improve HA particles' dispersity, which is one of the major factors affecting the mechanical properties of composite materials, various contents of citric acid were used for the preparation of HA/PVA films. At a citric acid concentration of 5 wt %, HA/PVA film with good dispersity of HA particles was obtained. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2007
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.