Abstract
In the case of bonding of aluminum alloy, surface pretreatment have been widely adopted for adherends so as to achieve superior adhesive performance. However, the strict surface treatment of the aluminum alloy cannot be implemented without special equipment and the mechanical properties, corrosion resistance and aging resistance of the common adhesives cannot meet the demand without surface treatment. Here, acrylic oligomer modified by carboxyl terminated organosilicon and nano alumina were used to modify an epoxy formulation based on a classical DGEBA monomer to produce a high peel strength epoxy adhesive that can be used without surface pretreatment. The peel strength and the shear strength of the adhesive could reach 7.18 N/cm and 18.75 MPa, respectively, and could be well maintained under −70 °C and 100 °C. The novel adhesive also has good heat aging resistance, water resistance and artificial seawater resistance. SEM and XPS were used to investigate mechanism of aging resistance of modified adhesives without surface treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.