Abstract
High nitrogen and nickel-free austenitic stainless steel has received much recognition worldwide because it can solve the problem of “nickel-allergy” and has outstanding mechanical and physical properties. In this article, 0Cr17Mn11Mo3N was prepared by powder injection molding (PIM) technique accompanied with solid-nitriding. The results show that the critical solid loading can achieve up to 64 vol% by use of gas-atomized powders with the average size of 17.4 μm. The optimized sintering conditions are determined to be 1300°C, 2 h in flowing nitrogen atmosphere, at which the relative density reaches to 99% and the N content is as high as 0.78wt%. After solution annealing at 1150°C for 90 min and water quench, the 0.2% yield strength, ultimate tensile strength (UTS), elongation, reduction in area, and hardness can reach as high as 580 MPa, 885 MPa, 26.0%, 29.1%, and Hv 222, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of University of Science and Technology Beijing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.