Abstract
Nanocomposite hydrogels based on tyramine conjugated gum tragacanth, poly (vinyl alcohol) (PVA), and halloysite nanotubes (HNTs) were prepared by electron beam irradiation and characterized. The FTIR, 1H NMR, and TGA results confirmed the chemical incorporation of HNTs into gum tragacanth. Gel content and swelling of hydrogels decreased with HNTs loading up to 20 % wt. The mechanical strength of hydrogels increased by increasing HNTs content up to 10 % with 371 kPa fracture stress at 0.95 fracture strain, compared to 312 kPa stress at 0.79 strain for gum tragacanth/PVA hydrogel. Hydrogel's biocompatibility and osteogenic activity were tested by seeding rabbit bone marrow mesenchymal stem cells. The cell viability was >85 % after 7 days of culture. In vitro secretion of ALP and calcium deposition on hydrogels in alizarin red assay after 21 days of culture indicated hydrogel potential for bone tissue engineering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.