Preparation of Gelatin Layer Film with Gold Clusters in Using Photographic Film

Abstract

A gelatin layer film with gold clusters is produced by taking advantage of the photosensitivity of silver halide photography. Through exposure silver specks, which are called latent-image specks and are composed of several reduced silver atoms, are formed on the surface of silver halide grains in the photographic film. As the latent-image specks act as a catalyst for redox reaction, reduced gold atoms are deposited on the latent-image specks when the exposed film is immersed in a gold (I) thiocyanate complex solution for 5–20 days. Subsequently, when the silver halide grains are dissolved and removed, the gelatin layer film with gold clusters remains. The film produced by this method is purple and showed an absorption spectrum having a maximum of approximately 560 nm as a result of plasmon absorption. The clusters continued to grow with immersion time, and the growth rate increased as the concentration of the gold complex solution was increased. The cluster diameter changed from 20 nm to 100 nm. By this method, it is possible to produce a gelatin film of a large area with evenly dispersed gold clusters, and since it is produced only on the exposed area, pattern forming is also possible.