Abstract
Biodegradable poly (lactide) (PLA) and poly (butylene adipate-co-terephthalate) (PBAT) composite films were made by a co-precipitation and hot-pressing method. The property of composite films like the chemical interaction, phase morphology, mechanical properties, and thermal properties were studied. The Fourier transform infrared spectroscopy (FTIR) test manifested that there was a small amount of the transesterifications between the PBAT and PLA during hot pressing, which could improve the compatibility of the two phases. The tensile strength of the film only reduced by 7.4%, while the elongation at break was increased by 119.1% compared with PLA after adding 4%wt PBAT. The composite films showed a high Ultraviolet-visible (UV) light barrier property. The UV blocking rate of the composite after adding 4%wt PBAT was 6.95 times higher than that of pure PLA at 380 nm. The PLA/PBAT composite films with excellent thermal stability, satisfactory mechanical properties and UV-light barrier have high a possibility for an UV screening packaging application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.