Abstract
Zn-Co(OH)2 precursor was hydrothermally deposited on carbon paper at 120°C, using cobalt nitrate and zinc nitrate as raw materials. Then Zn-Co(OH)2 was etched and partially sulfided into CoSOH/Co(OH)2 with 5 mol/L NaOH and 1 mol/L Na2S aqueous solution at room temperature. The catalytic performance in oxygen evolution reaction (OER) was investigated. XRD, SEM, TEM, XPS were used to characterize the microstructure, physical and chemical properties of the catalyst. The results show that the used method can etch Zn atoms, create oxygen vacancies and dope sulfur. The oxygen vacancies and doped sulfur play a positive role in enhancing the OER performance. In addition, amorphous CoSOH also exhibited better OER activity. The synergy between CoSOH and Co(OH)2 finally induces the best catalytic properties (overpotential η=310 mV, Tafel slope b=90 mV/dec) and long-term electrochemical stability, that is CoSOH/Co(OH)2 possess superior electrocatalytic oxygen evolution performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.