C/C-SiC brake materials were prepared by improved chemical liquid vaporized infiltration (CLVI) combined with liquid silicon infiltration (LSI) process, which needed less than thirty hours. The microstructure and frictional properties of the material were investigated. The density and porosity of the C/C-SiC brake material were 2.05 g/cm3 and 4.8%, respectively. The average dynamic friction coefficient of the materials was about 0.36, and the friction coefficient was stable. The average linear wear rate was less than 4.7 µm cycle-1 for rotating and stationary disk. The matrix composition and microstructure resulted in the high frictional performances.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.