Abstract
Core-shell ceramics fibers with multiple composition are ideal candidates for thermal insulation application at high temperature. Herein, ultrathin C–SiC/ZrSi x O y C z core-shell fibers were successfully fabricated by coaxial electrospinning and high temperature pyrolysis with polycarbosilane (PCS) as core precursor and Zirconium butoxide as shell precursor, respectively. The ceramics fibers revealed distinct core-shell partition. The average diameter was about 3 μm and the shell thickness increased to 500 nm with increasing pyrolysis temperature. Thermogravimetry analysis (TGA) results showed that the weight of the fibers reduced to 60% in Ar atmosphere and rose to 108% in O 2 atmosphere, which confirmed the excellent thermal stability and anti-oxidation properties due to the protection effect of shell layer and the self-healing mechanism. Moreover, the ceramics fibers maintained good flexibility and deformability. Such optimized anti-oxidation and mechanical performance indicates that the prepared core-shell fibers could be an excellent thermal insulation material for high temperature application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.