Abstract
In this study, (Ba1-x,Srx)TiO3 thin films of various composition ratios were deposited on glazed Al2O3 substrates by the CSD method, and the temperature dependence of the dielectric property was analyzed. The dielectric property of the BST (80/20) thin film annealed at C was highly tunable, and the temperature dependence of the dielectric constant was stabilized at around room temperature. However, this BST (80/20) thin film exhibited intense ferroelectricity. Its tan intensified to 0.0511 in the high-frequency range (1 MHz). After the BST thin film was annealed at 600C, the grain size of the BST thin film was reduced to 40 nm and the ferroelectricity was alleviated. The dielectric constant, tan, and tunability of the BST thin film at 100 kHz were 158, 0.0170, and 39.6 (214 kV/cm, 6.0 V), respectively. The change rate of the dielectric constant, which indicates its temperature dependence, was ±7 or less in the range of -55 to 85C. Therefore, this BST thin film was considered to guarantee a wide operation temperature range for microwave tunable devices.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.