Abstract
Both powder and film of apatite-type La 9.33(SiO 4) 6O 2 were prepared by alcoxide-hydrolysis. The apatite formation temperature was considerably lowered in this preparation method comparing to its solid-state reaction. Its sintered body did not show any particular orientation of the anisotropic apatite crystals. Electrical conductivity was 7.2 × 10 −5 S cm −1 at 500 °C. The films deposited on quartz glass and Pt substrates with thickness of either 1.0 or 1.5 μm had uniform microstructure extended on their surface. Preferred orientation of La 9.33(SiO 4) 6O 2 was observed on the surface of the film deposited on quartz glass substrate; its basal plane was parallel to the substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.