Abstract
Amino-functionalized graphene oxide (NGO) was prepared by Hoffman rearrangement where carboxyl group was replaced directly by amino group instead of using long-chain containing amino group. The chemical structure of NGO was studied by FT-IR, UV–vis, Raman, XPS and TGA. NGO was incorporated into polyacrylate latex (PA) by blending to prepare PA/NGO composite. The dispersibility of NGO in PA latex was significantly influenced by pH values. When the pH value was higher than 6, NGO uniformly dispersed in PA. The mechanical properties of the PA/NGO film were relayed on the pH. The break strength of the film was increased from ∼2 MPa to ∼5 MPa but the elongation at break decreased from 475% to 258% compared with those of PA film. The glass transition temperature (Tg) of PA/NGO film increased by 3.48 °C. For the sake of comparison, the mechanical properties and Tg of a similar composite but with bare graphene oxide (PA/GO) are presented.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.