Abstract
Poly (L-lactic acid)/organically modified montmorillonite (PLLA/OMMT) nanocomposites were fabricated by a solution intercalation method. OMMT, modified with quaternary alkylammonium ion, was prepared by alkyltrialkoxysilane. The differential scanning calorimetry measurement revealed that the crystallization temperatures of PLLA/OMMT nanocomposites were at around 110 °C regardless of the existence of OMMT or the weight fraction of them. X-ray diffraction patterns suggested that the (001) diffraction was around 2θ = 2.5°. The TEM image showed variously expanded interlayer galleries of OMMT and partially exfoliated silicate layer unit in the matrix. Board-shaped specimens for mechanical property tests were fabricated by compression-molding at 190 °C (including 30 min annealing at 110 °C). The flexural modulus of the nanocomposites increased with increasing content of OMMT. Vickers hardness of the nanocomposites were almost same independent on weight fraction of OMMT.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call