Abstract
In this study, we prepared and characterized Nb-doped Li7La3Zr2−xO12 (LLZNO) powder and pellets with a cubic garnet structure by using a modified sol-gel synthesis and hot pressing. LLZNO powder with a very small grain size and cubic structure without secondary phases could be obtained by using a synthesis method in which Li and La sources in a propanol solvent were mixed together with Zr and Nb sources in 2-methoxy ethanol. A pure cubic phase LLZNO pellet could be fabricated from the prepared LLZNO and an additional 6-wt% of Li2CO3 powder by hot pressing at 1050 °C and 15.8 MPa. The hot-pressed LLZNO pellet with a relative density of 99% exhibited a very dense surface morphology. The total Li ionic conductivity of the hot-pressed LLZNO was 7.4×10 −4 S/cm at room temperature, which is very high level compared to other reported values. The activation energy for ionic conduction was estimated to be 0.40 eV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.