Abstract

Vacuum induction melting is a more energy-efficient process for the preparation of a titanium alloy with good homogeneity and low cost. But the crucial problem for this technology is in developing a crucible refractory with high stability. In the present work, a novel (Ca,Sr,Ba)ZrO3 crucible was prepared by slip casting and its performance in melting NiTi alloy was studied. The results showed that a single solid solution was formed with a homogeneous distribution of metal elements after sintering at 1500 °C. It was found that the total content of oxygen and nitrogen remaining in the TiNi alloy after melting in the (Ca,Sr,Ba)ZrO3 crucible was 0.0173 wt.%, which fulfills the ASTM standard on biomedical TiNi alloys. The good resistance of the (Ca,Sr,Ba)ZrO3 crucible to molten NiTi has a relationship with the sluggish diffusion effect of high-entropy ceramics. This study provides insights into the process of designing highly suitable crucible material for melting a NiTi alloy.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.