Abstract
Cellulose microcrystalline (CMC), a linear polysaccharide with glucosidic bond, was successfully extracted from bamboo powder and modified by 3‐aminopropyltriethoxy silane coupling agent (KH550) to prepare KH550‐CMC. The prepared KH550‐CMC, in association with ammonium polyphosphate (APP), was introduced into epoxy resin (EP) by casting process to obtain flame retardant composites. The fire performance evaluation indicated that the presence of 10‐phr APP and 5‐phr KH550‐CMC in EP achieved the maximal LOI value of 28.9%, passed the UL‐94 V‐0 rating, and significantly decreased the peak heat release rate from 1055 kW/m2 of neat EP to 286 kW/m2. The improved fire performance is due to the improvement of dispersity of CMC in EP matrix and formation of better char layer, thus protecting the matrix effectively. Moreover, the introduction of KH550‐CMC could also partly eliminate the negative influence of flame retardants on the mechanical properties of EP composites due to the strengthening effect of CMC and better interfacial compatibility after modification with KH550.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.