Nanocomposite membranes based on the poly(vinyl alcohol) (PVA)/poly(sulfonic acid)-grafted silica nanoparticles (PSA-g-SN) were prepared via solvent casting of PVA cross linked by glutardialdehyde in the presence of various amounts (0–20 wt%) of silica nanoparticles (SN), poly(styrene sulfonic acid)- (PSSA-g-SN) and poly (2-acrylamido-2-methyl-1-propane sulfonic acid)-grafted silica nanoparticles (PAMPS-g-SN) as hydrophilic inorganic modifiers. PSA-g-SN nanoparticles were synthesized by surface-initiated redox grafting of SSA and AMPS monomers from the surface of the aminopropylated silica nanoparticles. Membranes were then characterized by FTIR, impedance spectroscopy, thermogravimetric analysis (TGA), water uptake, tensile strength test and SEM. The best proton conductivity was observed for membranes containing 5 wt% of nanoparticles. Among three nanoparticles used, the highest proton conductivity (10.4 mS/cm) was observed for PVA membrane prepared in the presence of 5 wt% PAMPS-g-SN nanoparticles. Results showed that grafting of sulfonated monomer onto the silica nanoparticles enhances various properties, for example proton conductivity, of the polymer electrolyte membranes (PEMs).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.