Abstract
Sm0.95Ho0.05FeO3 was successfully prepared in a single phase using the citrate combustion method. The investigated sample was characterized using X-ray diffraction (XRD), a high-resolution transmission electron microscope (HRTEM) and X-ray photoemission spectroscopy (XPS). XRD confirmed that the sample was synthesized in an orthorhombic phase with an average crystallite size of 12 nm. HRTEM indicated that the sample was prepared in the nanoscale with an average particle size of 18 nm. XPS was used to identify the chemical bonds, binding energies and core levels of Sm0.95Ho0.05FeO3. The magnetic properties were studied using a vibrating sample magnetometer and DC magnetic susceptibility using Faraday’s method. The sample has an antiferromagnetic behavior with weak ferromagnetic components. The presence of magnetic Ho3+ ions in the SmFeO3 sample causes the magnetic exchange interaction between the 2p orbital of Fe3+ and the 4d sub-shell of Ho3+ ions. The dependence of pH value on the removal efficiency of Pb2+ from water was studied. The maximum Pb2+ removal efficiency of the Ho-doped SmFeO3 nano perovskite is 26% at pH = 5 and 99% at pH = 8. The Freundlich, Langmuir and Temkin isotherms were studied to understand the adsorption mechanism. The Temkin adsorption isotherm best fitted with the experimental data.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.