Abstract
Calcium oxalate crystals in urine often differ in size and crystal phase between healthy humans and patients with kidney stones. In this work, calcium oxalate monohydrate (COM) and dihydrate (COD) with sizes of about 50 nm, 100 nm, 1 μm, 3 μm, and 10 μm were prepared by varying reactant concentration, reaction temperature, solvent, mixing manner, and stirring speed. These crystals mainly had a smooth surface and no obvious pore structure, except COM-1 μm. In cell culture medium, the zeta potential of crystals became increasingly negative with increasing size, and the absolute value of zeta potential of COD was greater than the same-sized COM. Results of cell viability and PI staining assays showed that the order of injury degree in African green monkey renal epithelial (Vero) cells caused by different sizes of COD was COD-50 nm>COD-100 nm>COD-1 μm>COD-3 μm>COD-10 μm, and that of different sizes of COM was COM-1 μm>COM-50~COM-100 nm>COM-3 μm>COM-10 μm. COM-1 μm presented the highest cytotoxicity in Vero cells, which was associated with its rougher surface, larger specific surface area (SBET), and larger pore volume. Overall, these findings indicated that the physical properties of crystals play an important role in their cytotoxicity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.