Abstract
The NiCuZn ternary coating was electrochemically deposited on a copper electrode. Then, it was etched in a concentrated alkaline solution (30% NaOH) to produce a porous and electrocatalytic surface suitable for use in the hydrogen evolution reaction (HER). The surface composition of coating before and after alkaline leaching was determined by energy dispersive X-ray (EDX) analysis. The surface morphologies were investigated by scanning electron microscopy (SEM). The long-term stability of electrode prepared for alkaline water electrolysis was investigated in 1 M KOH solution with the help of cathodic current-potential curves and electrochemical impedance spectroscopy (EIS) techniques. It was found that, the NiCuZn coating has a compact and porous structure with good physical stability. Alkaline leaching process further improved the activity of NiCuZn coating in comparison with binary NiCu deposit for the HER. The long-term operation at −100 mA cm −2 showed good electrochemical stability over 120 h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.