Abstract
Present study illustrates the preparation of chitin nanofibrils (CNF) reinforced carrageenan nanocomposite films by the solution-casting technique. CNF was prepared by acid hydrolysis of chitin, followed by high speed homogenization and sonication. FTIR result demonstrated that the chemical structure of chitin had not changed after acid hydrolysis. However, the crystalinity of CNF was found to be higher than chitin. The crystallite size of chitin and CNF was 4.73 and 6.27 nm, respectively. The char content at 600 °C of chitin (19.2%) was lower than the CNF (25%). The carrageenan/CNF composite films were smooth and flexible and the CNF was dispersed uniformly in the carrageenan polymer matrix. The tensile strength and modulus of carrageenan film were increased significantly (p<0.05) after CNF reinforcement with up to 5 wt%, however, elongation at break, water vapor permeability, and transparency decreased slightly. Carrageenan/CNF nanocomposite films showed strong antibacterial activity against a Gram-positive food-borne pathogen, Listeria monocytogenes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.