In this paper an adaptive Ni-Mo-Al-Ag-BN composite coating was deposited by plasmaspraying. Its tribological property from 20°C-600°C were evaluated by using high temperature tribometer. Scanning electron microscopy and Raman spectroscopy were used to characterize the coating and corresponding wear tracks to determine the lubrication mechanisms. The result shows that the friction coefficient of the Ni-Mo-Al–Ag-BN composite coating from 200°C to 400°C is about 0.4 and declines very slightly at 600°C . The wear rates of the coating is 2.0×10-4mm3/N*m at 600°C and the downward trend is obvious compared with 400°C. Silver provide lubrication below 400 °C. Ag2MoO4 were formed with the temperature raised, and acted as high-temperature lubricants above 400 °C. Ni-Mo-Al–Ag-BN composite coating established a new lubrication mechanism model at 600°C . It can be concluded that the plasma sprayed Ni-Mo-Al - Ag - BN composite coating can keep good tribological property at wide range of temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.