Preparation and thermal properties of polyphenylene sulfide/organic montmorillonite composites

Abstract

Cetyl trimethyl ammonium bromide (CTAB) was used for the intercalation modification of nano-montmorillonite (MMT). The spectra of Fourier transform infrared spectrometer (FTIR) and X-ray diffraction (XRD) suggested that CTAB had intercalated into the layers of MMT. And the interlayer spacing of MMT increased from 1.198 to 3.616 nm. The thermogravimetric analysis (TGA) curves of organic montmorillonite (OMMT) showed three-step degradation. The scanning electron microscope (SEM) photographs showed that surface morphology of MMT remained unchanged. Then polyphenylene sulfide (PPS)/organic montmorillonite (OMMT) composites were prepared by melt blending. And composites were treated at 180 °C for 24 h. The results of SEM showed that OMMT had good dispersion behavior and adhesion with PPS. The results of differential scanning calorimetry (DSC) showed the addition of OMMT resulted in heterogeneous nucleation crystallization of PPS. The results of TGA showed there was a good improvement of the thermal stability of PPS. The FTIR and color measurement analysis showed the addition of OMMT could improve the thermal oxidation stability.