Abstract
SiCw-SiC foams with hollow skeleton were synthesized by a simple procedure that consisted of the chemical vapor infiltration (CVI) and oxidation process. Flexible carbon foam was employed as CVI template. A typical structure of SiCw-SiC foams consisting of SiC supporter with hollow skeleton structure accompanying numerous crooked SiC whiskers was obtained after burning out carbon skeleton of the carbon foam during oxidation process. SiCw-SiC foams have a density of 0.11≤ρ≤0.12g/cm3, porosity ≥96% and a thermal conductivity at room temperature between 0.040 and 0.075W/m·K. Thermal conductivity of the SiCw-SiC foams moderately increased with elevation of temperature, indicating that these foams with larger amount of whiskers exhibit excellent thermal insulation property at elevated temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.