Abstract
Single phase CoO, NiO, and Ni0.5Co0.5O epitaxial films have been prepared by reactive sputtering onto 〈0001〉 α−Al2O3 substrates maintained at 373 K. Epitaxy was confirmed by x-ray diffraction (XRD) and high resolution electron microscopy (HREM) techniques. XRD experiments indicate that these monoxide films are cubic and contain rotation twins with the twin axis parallel to 〈111〉. Lattice parameters for the CoO and NiO films are 0.4254 ± 0.0001 nm and 0.4173 ± 0.0006 nm, respectively, and agree with published values for the corresponding bulk oxides. The lattice parameter 0.4220 ± 0.0001 nm for the Ni0.5Co0.5O film lies between those of CoO and NiO and suggests that the mixed oxide film is compositionally homogeneous. Cross-sectional HREM images of the Ni0.5Co0.5O specimen show Σ3(12) twin boundaries perpendicular to the oxide-substrate interface. The twin regions are approximately 30 nm in size and are uniformly distributed throughout the film. The epitaxial orientation of the monoxide films with respect to the substrate can be summarized by the relationships [111] monoxide // [0001] α−Al2O3, [10] monoxide // [100] α−Al2O3, and [11] monoxide // [110] α−Al2O3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.