Abstract
Silicon-rich silicon nitride thin films are prepared on P-type monocrystalline silicon wafer (100) and glass substrate by plasma chemical vapor deposition with reaction gas sources SiH4 and NH3. The deposited samples are thermally annealed from 600°C to 1000°C in an atmosphere furnace filled with high purity nitrogen. The annealing time is 60 minutes. Fourier transform infrared spectroscopy (FTIR) is carried out to investigate the bonding configurations in the films. The results show that the Si-H bond and N-H bond decrease with the increase of annealing temperature, and completely disappear at the annealing temperature of 900°C. But the Si-N bond is enhanced with the increase of annealing temperature, and the blue shift occurs, then Si content in the film increases. The Raman Spectra show that the amorphous Si Raman peak appears at 480 cm-1 in the film at 700°C. The Raman spectra of the films annealed at 1000 °C is fitted with two peaks, and a peak at 497 cm -1 is found, which indicated that the Si phase in the films changed from amorphous to crystalline with the increase of annealing temperature. The experiment also analyses the luminescence properties of the samples through PL spectrum, and it is found that there are five luminescence peaks in each sample under different annealing temperature. Based on the analysis of Raman spectrum and FTIR spectrum, the PL peak of amorphous silicon quantum dots appears at the wavelength range of 525-555nm, and the other four PL peaks are all from the defect state luminescence in the thin films, and the amorphous silicon quantum dot size is calculated according to the formula.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.