Preparation and properties of poly[styrene‐co‐(butyl acrylate)‐co‐(acrylic acid)]/silica nanocomposite latex prepared using an acidic silica sol

Abstract

AbstractBACKGROUND: Polyacrylate/silica nanocomposite latexes have been fabricated using blending methods with silica nanopowder, in situ polymerization with surface‐functionalized silica nanoparticles or sol–gel processes with silica precursors. But these approaches have the disadvantages of limited silica load, poor emulsion stability or poor film‐forming ability.RESULTS: In this work, poly[styrene‐co‐(butyl acrylate)‐co‐(acrylic acid)] [P(St‐BA‐AA)]/silica nanocomposite latexes and their dried films were prepared by adding an acidic silica sol to the emulsion polymerization stage. Morphological and rheological characterization shows that the silica nanoparticles are not encapsulated within polymer latex particles, but interact partially with polymer latex particles via hydrogen bonds between the silanol groups and the COOH groups at the surface of the polymer particles. The dried nanocomposite films have a better UV‐blocking ability than the pure polymer film, and retain their transparency even with a silica content up to 9.1 wt%. More interestingly, the hardness of the nanocomposite films increases markedly with increasing silica content, and the toughness of the films is not reduced at silica contents up to 33.3 wt%. An unexpected improvement of the solvent resistance of the nanocomposite films is also observed.CONCLUSION: Highly stable P(St‐BA‐AA)/silica nanocomposite latexes can be prepared with a wide range of silica content using an acidic silica sol. The dried nanocomposite films of these latexes exhibit simultaneous improvement of hardness and toughness even at high silica load, and enhanced solvent resistance, presumably resulting from hydrogen bond interactions between polymer chains and silica particles as well as silica aggregate/particle networks. Copyright © 2009 Society of Chemical Industry