Preparation and Properties of Gel Polymer Electrolytes with Li1.5Al0.5Ge1.5(PO4)3 and Li6.46La3Zr1.46Ta0.54O12 by UV Curing Process.

Abstract

Poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP)-based gel polymer electrolytes (GPEs) are considered a promising electrolyte candidate for polymer lithium-ion batteries (LIBs) because of their free-standing shape, versatility, security, flexibility, lightweight, reliability, and so on. However, due to problems such as low ionic conductivity, PVDF-HFP can only be used on a small scale when used as a substrate alone. To overcome the above shortcomings, GPEs were designed and synthesized by a UV curing process by adding NASICON-type Li1.5Al0.5Ge1.5(PO4)3 (LAGP) and garnet-type Li6.46La3Zr1.46Ta0.54O12 (LLZTO) to PVDF-HFP. Experimentally, GPEs with 10% weight LLZTO in a PVDF-HFP matrix had an ionic conductivity of up to 3 × 10-4 S cm-1 at 25 °C. When assembled into LiFePO4/GPEs/Li batteries, a discharge-specific capacity of 81.5 mAh g-1 at a current density of 1 C and a capacity retention rate of 98.1% after 100 cycles at a current density of 0.2 C occurred. Therefore, GPEs added to LLZTO have a broad application prospect regarding rechargeable lithium-ion batteries.