Abstract
Double perovskite oxides with mixed ionic and electronic conductors (MIECs) have been widely investigated as cathode materials for solid oxide fuel cells (SOFCs). Classical Fe-based double perovskites, due to their inherent low electronic and oxygen ionic conductivity, usually exhibit poor electrocatalytic activity. The existence of various valence states of B-site ions modifies the material’s catalytic activity, indicating the possibility of the partial substitution of Fe by higher-valence ions. LaBaFe2−xMoxO5+δ (x = 0, 0.03, 0.05, 0.07, 0.1, LBFMx) is used as intermediate-temperature solid oxide fuel cell (IT-SOFC) cathode materials. At a doping concentration above 0.1, the Mo substitution enhanced the cell volume, and the lattice expansion caused the formation of the impurity phase, BaMoO4. Compared with the parent material, Mo doping can regulate the oxygen vacancy concentration and accelerate the oxygen reduction reaction process to improve the electrochemical performance, as well as having a suitable coefficient of thermal expansion and excellent electrode stability. LaBaFe1.9Mo0.1O5+δ is a promising cathode material for IT-SOFC, which shows an excellent electrochemical performance, with this being demonstrated by having the lowest polarization resistance value of 0.017 Ω·cm2 at 800 °C, and the peak power density (PPD) of anode-supported single-cell LBFM0.1|CGO|NiO+CGO reaching 599 mW·cm−2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.