Preparation and properties of epoxy resins cured with silyl esters of phenol novolak and cresol novolak

Abstract

The curing agents of epoxy resin, trimethylsilyl ethers of phenol novolak (TMSPN) and cresol novolak (TMSCN) were prepared by refluxing phenol novolak and cresol novolak respectively, with the mixture of hexamethyldisilazane and chlorotrimethylsilane in THF. The curing reaction of epoxy resin with these curing agents and the thermal properties of cured resins were examined. The Tg values of epoxy resins cured with TMSPN were a little higher than those cured with TMSCN. The maximum of Tg is 118°C for TMSPN-cured epoxy resin against 112°C for TMSPN-cured epoxy resin. The water absorption of hydrophobic epoxy resins cured with TMSPN was a little lower than those cured with TMSCN. The clear decrease of water absorption is attributed to the difficulty of the micro-void formation caused by the more tight primary structures of TMSPN. The water absorption at 25°C containing trimethylsilyl groups is about one-tenth of that of epoxy resins cured with conventional curing agents and even one-half of that of the epoxy resins cured with active esters. The low water absorption is attributed to the presence of trimethylsilyl groups, which are more hydrophobic than ester groups, and to the absence of hydroxyl groups of the cured resins.