Abstract
The investigated low temperature Co fired ceramics(LTCC) composite of 60wt% CaO-Al2O3-B2O3-SiO2 glass and 40wt% α-Al2O3 as a filler is a non-reactive system, which is a critical part of the low temperature Co fired ceramics process. Through a study on densification process, the phase transformation and microstructure can be revealed. Its composites typically consist of CaO-Al2O3-B2O3-SiO2 glass and α-Al2O3 powders of average particle size (D50=3.49 μm). The sintering behavior, phase evaluation, sintered morphology, and microwave dielectric properties were investigated. In the fire range of 800 to 900 °C, the composites were crystallized after completion of densification. It is found that the composites start to densify at 825 °C, simultaneously, the dielectric constant (ɛr) reaches its maximum. With increasing heat-treatment temperatures, due to the loose microstructure of the material, tanδ increases slightly. The last of the sintered samples were identified as partly Anorthite at 850 °C. At that temperature it has ɛr of 7.9 and tanδ less than 1×10−3, and can be used as a promising LTCC material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.