Abstract
A new series of core–shell structured silver/polyimide (PI) nanocomposites was prepared by in situ polymerization followed by the chemical imidization of poly(amic acid) (PAA, precursor of PI) at a low temperature. The TEM images showed that the silver cores of the nanocomposites were encapsulated with homogeneous shells with thickness of 4 and 8 nm at silver contents of 90 and 60 %, respectively. The shell thickness was controlled by varying the content of PAA. FTIR spectroscopic analysis indicated that the imide ring formation occurred after the chemical imidization. The Ag/PI nanocomposites showed excellent thermal stability and exhibited only 10 % weight loss at 300 °C in the air. Moreover, percolation was observed at silver weight fractions close to the critical value, and the maximum dielectric permittivity of the nanocomposites was 120, which is about 40 times higher than that of pristine PI.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.