Abstract
Electrically conducting arachidic acid/polypyrrole (PPy) composite films were prepared by exposing the arachidic acid LB films containing ferric chloride to pyrrole vapor. The optimum conditions to deposit matrix LB film were the subphase temperature of 23–25°C, pH of 6.0 and ferric chloride concentration of 5.0 × 10−5 M. The formation of PPy in the arachidic acid matrix LB films was confirmed by UV-visible spectra, FTIR spectra, and scanning electron micrographs. The average thickness of the composite LB films prepared at 0°C was 1525 Å. The composite films prepared at lower temperatures have more uniform surface and exhibit higher electrical conductivity than the films prepared at higher temperatures do. The in-plain conductivity and the transverse conductivity of the composite film were 10−3−10−2 S/cm and 10−6S/cm, respectively, and, thus, the conductivity anisotropy was about 103 © 1996 John Wiley & Sons, Inc.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.