Abstract
In this work, the synthesis of CoFe2O4 via sol-gel auto-combustion method, using iron nitrate, cobalt nitrate and citric acid, with subsequent heat treatment in air was studied. The effects of the molar ratio of the metal nitrates to citric acid and the heat treatment temperatures on the magnetic properties have been investigated. The X-ray diffraction patterns showed peaks consistent with cubic spinel-type structure. The average crystallite sizes were determined from the (311) peak of the diffraction pattern using Scherrer equation. Particle sizes in the range of 18-44 nm were obtained. The crystallite size increases with annealing temperature. Magnetic properties, such as saturation magnetization (Ms), remanent magnetization (Mr) and coercivity field (Hc) were measured at room temperature using a vibrating sample magnetometer. Saturation magnetization was found to increase with particle size, whereas coercivity was found to reduce exponentially as the particle size was increased, apart from the Hc of the sample treated at 300 °C. The present work shows that magnetic properties vary over a wide range by changing the synthesis conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.