Abstract
AbstractA nanocomposite energetic material was prepared using sol‐gel processing. It was incorporated into the nano or submicrometer‐sized pores of the gel skeleton with a content up to 95 %. AP, RDX, and silica were chosen as the energetic crystal and gel skeleton, respectively. The structure and its properties were characterized by SEM, BET methods, XRD, TG/DSC, and impact sensitivity measurements. The structure of the AP/RDX/SiO2 cryogel is of micrometer scale powder with numerous pores of nanometer scale and the mean crystal size of AP and RDX is approx. 200 nm. The specific surface area of the AP/RDX/SiO2 cryogel is 36.6 m2 g−1. TG/DSC analyses indicate that SiO2 cryogel can boost the decomposition of AP and enhance the interaction between AP and RDX. By comparison of the decomposition heats of AP/RDX/SiO2 at different mass ratios, the optimal mass ratio was estimated to be 6.5/10/1 with a maximum decomposition heat of 2160.8 J g−1. According to impact sensitivity tests, the sensitivity of the AP/RDX/SiO2 cryogel is lower than that of the pure energetic ingredients and their mixture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.