Abstract
Chemical liquid-vapor deposition (CLVD) process is a new style of fast densification, which combines the advantages of PIP process and CVI process. 2D C/SiC composites were prepared at 800~1200°C for 3~4 hours with liquid polycarbosilane and carbon fiber cloth by CLVD process with induction heating, and had the density of 1.7 g/cm3, the flexural strength of 84.6MPa, and the flexural modulus of 20GPa. XRD pattern of the sample proved that the matrix was β-SiC. It was found that SiC deposited mainly around single fiber instead of among fiber bundles and layers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.