Abstract
The S-sulfo keratin was extracted from wool and was then spray-dried to give S-sulfo keratin powder. differential scanning calorimetry analysis showed that the glass transition temperature of S-sulfo keratins became lowered with the increase of moisture content, while perfectly dried S-sulfo keratin powder did not give thermal transition in the temperature range 30–130°C. The compression molding of the S-sulfo keratin powder supplemented with one-tenth weight of water afforded a plastic-like transparent proteinous film above the glass transition temperature. The film obtained from the powder without water addition or compression molded below glass transition temperature partly remained powdery. The film compression molded at 120°C gave the maximum ultimate strength and Young’s modulus, 27.8±2.9 and 1218±80 MPa, respectively. Obtained film was insoluble and slightly swelled in water, but, in the presence of reducing agent, the film significantly swelled at pH 7.0 and even dissolved at pH 9.0, suggesting the relevance of abundant disulfide linkage. The film supported the mammalian cell adhesion and proliferation, demonstrating the biocompatibility of S-sulfo keratin films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.