Abstract
Highly ordered TiO2 nanowire (TN) arrays were prepared in anodic alumina membranes (AAMs) by a sol-gel method. The TNs are single crystalline anatase phase with uniform diameters around 60 nm. At room temperature, photoluminescence (PL) measurements of the TN arrays show a visible broadband with three peaks, which are located at about 425, 465, and 525 nm that are attributed to self-trapped excitons, F, and F+ centers, respectively. A model is also presented to explain the PL intensity drop-down of the TN arrays embedded in AAMs: the blue PL band of AAMs arises from the F+ centers on the pore walls, and the TNs first form in the center area of the pores and then extend to the pore walls.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.