Abstract
The phenolic(PF) foams were prepared used low-temperature foaming and curing method. The optimum low-temperature foaming processing technology conditions and material proportioning were described below. The curing temperature was 40 °C, the amount of foaming agent iso-pentane was 8-10wt.%, tween-80 dosage was 6-7wt.%, the amount of composite curing agent was 15-18wt.%.The effects of low-temperature foaming on mechanical properties, heat insulation, fire-retardant, foam hole form and micro-structure were discussed. 40°C and 70°C curing PF foam performance comparison results showed that low-temperature curing technology slightly affect the fire-retardant properties of PF foam. And excellent overall performance PF foam were prepared with 40°C foaming technology, the foam hole morphology structure, toughness and strength of PF foam were better. In addition, the low-temperature curing PF foam had more even foam hole distribution, more regular foam hole structure, more clean foam hole arrangement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have