Abstract
ABSTRACTThe preparation and oxygen permeability of composites of Ce0.8Gd0.2O2-ö (GDC) and spinel-type ferrites, MFe2O4 (M = Co and Mn) have been investigated. The composites of GDC -x vol% MFe2O4, where x ranged from 5 to 65, were prepared by a citrate-based liquid-mix technique. The composites were found to be almost fully densified by sintering at 1300 °C for 2 h. From TEM observations, the grain size of GDC and spinel-type phases was found to be less than 0.5 μm. In the case of M = Co, GDC - 25 vol% CoFe2O4 with a membrane thickness of 1.0 mm exhibited an oxygen flux density of 0.21 μmol·cm-2·s-1 under the P(O2) difference between He (20 sccm) and air at 1000 °C. Under reducing atmosphere of Ar-5%H2, the oxygen flux density of this composite increased up to 1.3 μmol·cm-2·s-1. Moreover, under Ar-10%CH4 gas flow, GDC - 15 vol% MnFe2O4 with a membrane thickness of 0.24 mm exhibited the oxygen flux density of 2 and 7 μmol·cm- · s- at 800 and 1000 °C, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.