Abstract
Four Pt-modified NiCrAlY coatings with different thicknesses and Re contents diffusion barrier (DB) were prepared on a single crystal superalloy by sequential treatments of Ni-Re co-electrodeposition, arc ion plating and Pt electrodeposition. To explore the effect of different forms of the Re-base DB on the oxidation resistance and interdiffusion behavior in Pt-modified NiCrAlY coating, the isothermal oxidation behavior of the four coatings at 1050 °C was investigated. The results indicated that Re-base DB can effectively improve the high-temperature oxidation resistance of Pt-modified NiCrAlY coating by inhibiting the internal diffusion of Al as well as the external diffusion of refractory elements. The coating samples of 5 µm Ni-45Re (at%) DB exhibited the lowest interdiffusion extent and the best long-term stability. Higher Re content DB tended to form layered σ-(Cr,Re) phase, while DB with lower content could only form granular σ-(Cr,Re) phase. The influence of different micromorphologies of the σ-phase on the long-term stability of DB was discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.