ABSTRACTPure Ge epitaxially grown on Si (100) at high temperatures forms typically 100 nm lateral size islands on top of a 3–4 monolayer thick wetting layer. In stacked layers of Ge dots pronounced vertical alignment is observed if the thickness of the Si spacer layers is smaller than about 50 nm. Pregrowth of a small amount of C on Si substrate induces very small 10 nm size Ge quantum dots after deposition of about 2 to 3 monolayers Ge. Photoluminescence (PL) studies indicate a spatially indirect radiative recombination mechanism with the no-phonon line strongly dominating. Strong confinement shift in the 1–2 nm high and 1Onm lateral size dots results in low activation energies of 30 meV, which causes luminescence quenching above 50K.For large stacked Ge islands with 13 nm thin Si spacer layers we observe a significantly enhanced Ge dot-related PL signal up to room temperature at 1.55μm wave length. This is attributed to a spatially indirect transition between heavy holes confined within the compressively strained Ge dots and two-fold degenerated Δ state electrons in the tensile strained Si between the Ge stacked dots.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.