Abstract
The LaxHo2-xFe17 (x=0.0, 0.2, 0.4, 0.6, 0.8) powders were prepared by arc melting and high energy ball milling. The influence of the La substitution on phase structure, morphology, magnetic properties and electromagnetic parameters were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), vibrating-sample magnetometry (VSM) and vector network analyzer (VNA), respectively. The results show that the saturation magnetization increases and the average particle size increases with the increase of La content. The minimum absorption peak frequency shifts towards a lower frequency region with the increase of La content. The minimum reflection loss (RL) of La0.2Ho1.8Fe17 reaches –28.72 dB at 8.72 GHz, and the frequency bandwidth of RL<–10 dB reaches about 2.32 GHz with the best matching condition d=1.8 mm. The reflection loss with the thickness ranging of 1.2∼2.4 mm could reach –10 dB, which indicates that the particles are considered as the promising microwave absorbing materials with better absorption properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.