Abstract
Bi2Sr2Co2Oy thin films were grown on 10° vicinal-cut Al2O3 (0001) single crystalline substrates by pulsed laser-deposition techniques with in situ annealing, post-annealing and non-annealing process, respectively. The pure phase Bi2Sr2Co2Oy thin film was obtained with a non-annealing process. The result of X-ray diffraction showed that Bi2Sr2Co2Oy thin film was obviously c-axis preferred orientation. The laser-induced thermoelectric voltage signals were detected in Bi2Sr2Co2Oy thin films, which originated from the anisotropy of the Seebeck coefficient. The maximum peak value of laser-induced thermoelectric voltage was strong and could reach as large as 0.44 V and the response time was 1.07 μs when the deposition time was 6 min. Furthermore, the peak voltage enhanced linearly with the single-pulse laser energy. These characteristics demonstrate that Bi2Sr2Co2Oy thin film is also an excellent choice for laser energy/power detectors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.