Abstract
In this paper, the adsorption characteristics of cationic polyelectrolyte PDADMAC on BGF particles and Zeta potential of BGF particles have been investigated. A new type of composite abrasive slurry was obtained with cationic polyelectrolyte modified BGF particles and its polishing performance was studied. Experimental results showed that the Zeta potential of the modified BGF particles was changed from negative to positive and the maximum value (+35mv) was obtained when the adsorption saturation was achieved, and the adsorption capacity of SiO2 abrasives on BGF particles was improved significantly as well. The material removal rate was 469nm/min with the modified BGF/ SiO2 composite abrasives slurry containing 5% SiO2 and 3% modified BGF particles, increasing by 47% and 89% than those of the unmodified BGF/SiO2 composite abrasives slurry (319nm/min) and the single silica abrasives slurry (248nm/min), respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.