Abstract
A series of M-type strontium hexaferrite powders with substitution of Mn 2+, Ni 2+ and Ti 4+ ions for Fe 3+ ions according to the formula SrFe 9(Mn 0.5− x Ni x Ti 0.5) 3O 19, where x ranges from 0 to 0.5 with a step of 0.1, has been prepared via the conventional ceramic method. In order to get nanoparticles, the obtained powders were milled in a high energy SPEX mill for 1 h. XRD investigations of the unmilled and milled powders show that the prepared samples are all single phase hexaferrite. Lattice parameters and mean crystallite sizes of the powders were determined from the XRD data and Scherrer’s formula. Transmission electron microscope (TEM) was used to analyze their structures. Room temperature magnetizations and coercivities of the samples in a magnetic field of 15 kOe have been determined from the hysteresis loops. It was found that magnetizations of the milled samples were smaller than the magnetization of the unmilled samples. This decrease, based on core–shell model, has been attributed to the presence of a magnetically dead layer on the particles’ surface of the milled powders. In addition, the magnetizations of the milled samples decrease with the increase in x value. This decrease has been discussed according to site occupation of the substituted cations on the sublattices. The discussion also supports the increase of lattice parameters and the decrease of Curie temperature as x increases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.