Preparation and Enhanced Thermoelectric Performance of Cu2Se–SnSe Composite Materials

Abstract

A series of p-type xCu2Se–SnSe (x = 0%, 0.10%, 0.15%, 0.20%, and 0.25%) composite thermoelectric materials have been prepared by the combination of ultrasonic dispersion and spark plasma sintering methods. The effects of secondary phase Cu2Se on the phase composition, microstructure, and thermoelectric properties of the composites were investigated. Microstructure characterization and elemental maps indicated Cu2Se grains uniformly distributed on the boundaries of the matrix. Transport measurements demonstrated that enhancement of the power factor and reduction of the thermal conductivity can be realized simultaneously by optimizing the adding content of Cu2Se. The highest ZT value of 0.51 at 773 K was achieved for the sample with x = 0.15%, increased by 24% compared with that of the SnSe matrix. These results demonstrate that optimizing the Cu2Se content can improve the thermoelectric performance of p-type SnSe polycrystalline materials.